GC Gold Label 1 Luting & Lining GIC

• Intrinsic chemical adhesion to both tooth structure and metal
• Glass Ionomer formulation
• Fluoride release
• High mechanical strength
• Excellent wetting properties
• Film thickness of just 15 microns
• Radiopaque
• Sharp set characteristics
• Low solubility
• Long term clinical data
• No surface preparation or bonding agent required
• Easy post-operative checks

A Strontium-based Glass Ionomer:
All GC Gold Label Glass Ionomer contains strontium glass.The strontium glass provides good radiopacity and snapset characteristics, unanimously preferred by clinicians around the world. Interestingly, strontium will mimic calcium in the formation of strontium hydroxyapatite and strontium fluoroapatite to affect internal remineralization within the tooth structure.

Surface Strengthening Effect:
Research has shown that a strontium-based glass ionomer placed in calcium-containing environment (saliva) will result in calcium ion diffusing into the glass ionomer&surface achieving a surface strengthening effect. All GC& Gold Label Glass Ionomer strengthens over time in saliva.

A Consistent Predictable Seal:
All GC Gold Label Glass Ionomer will display a glossy& surface after mixing. This indicates sufficient free polyacrylic acid is available to begin the ion exchange process. The& subsequent movement of ions between dentin, enamel and& GC Glass Ionomer creates an ion exchange zone which chemically fuses them together. The resulting seal is& consistent, predictable and long lasting.

INDICATIONS :

• Cementation of metal or porcelain fused to metal crowns, bridges, inlays
• Cementation of stainless steel crowns or orthodontic appliances retained with stainless steel crowns
• Cementation of orthodontic bands
• Base or liner

ADVANTAGES:

• Allows minimal cavity preparation
• Less stress on margins and marginal seal
• Protects against secondary caries
• Promotes internal remineralization and surface strengthening
• Easy post-operative diagnosis
• Easier mixing and sharper setting makes it so easy to use
• Final finish may be completed under water 15 minutes from start of mix
• Matches to natural tooth structure
• Good colour match to tooth structure
• More durable, longer lasting restorations
• Assurance of successful restorations

Composition / Information on Ingredients
(% chemical components by WT)

• Distilled water (CAS 7732-18-5) 50-55%
• Polyacrylic acid (CAS 9003-01-4) 30-40

Store at temperature of 4-25°C (39.2-77.0°F)

Powder/liquid ratio (g/g) 1.4/1.0 1.8/1.0 2.2/1.0
Mixing time (min. sec.) 20" 20" 20"
Working time (min. sec.) 2’30" 2’00" 1’15"
Net setting time (min. sec.) 2’50" 2’30" 2’20"

PRECAUTIONS

• In case of contact with oral tissue or skin, remove immediately with a sponge or cotton soaked in alcohol. Flush with water.
• In case of contact with eyes, flush immediately with water and seek medical attention.
• DO NOT mix powder or liquid with any other glass ionomer components.

Gc Gold Label 1 Glass Ionomer Big Pack:

• 1 x 35g Powder
• 1 x 25g Liquid
• 1 x Mixing Pad

• STEP1- Mix to the correct powder: liquid ratio (20 seconds for Gold Label 1)
• STEP2- Apply the mixed cement to both restoration and prepared tooth
• STEP3- Seat the restoration within 30 seconds of completing the mix
• STEP4- Remove the excess cement during the gel stage Total setting time is 4’30” after the start of a mix
• STEP5- After the final set, moisture-proof the margin by applying a final coat of GC Fuji Varnish or GC Fuji Coat LC